Внимание!

В связи с проведением технических работ возможно замедление работы Электронной библиотеки, некоторые коллекции будут временно недоступны

Logo BSU

Please use this identifier to cite or link to this item: https://elib.bsu.by/handle/123456789/271097
Full metadata record
DC FieldValueLanguage
dc.contributor.authorЧернов, И. И.
dc.contributor.authorСтальцов, М. С.
dc.contributor.authorКалин, Б. А.
dc.contributor.authorДжумаев, П. С.
dc.contributor.authorДиков, А. С.
dc.contributor.authorИванов, И. А.
dc.date.accessioned2021-10-28T08:18:56Z-
dc.date.available2021-10-28T08:18:56Z-
dc.date.issued2021
dc.identifier.citationВзаимодействие излучений с твердым телом : материалы 14-й Междунар. конф., посвящ. 100-летию Белорус. гос. ун-та, Минск, Беларусь, 21-24 сент. 2021 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2021. – С. 237-241.
dc.identifier.issn2663-9939 (Print)
dc.identifier.issn2706-9060 (Online)
dc.identifier.urihttps://elib.bsu.by/handle/123456789/271097-
dc.descriptionСекция 2. Радиационные эффекты в твердом теле = Section 2. Radiation Effects in Solids
dc.description.abstractС помощью просвечивающей электронной микроскопии (ПЭМ) изучено влияние облучения высокоэнергетическими ионами Fe 10+ и Ni 11+ при 650 о С до дозы 100 сна на развитие вакансионной пористости, изменение химического и структурно-фазового состава стали 08Х18Н10Т. Обнаружено двугорбое распределение пор по размеру по глубине мишеней, что вызвало два максимума распухания на расстояниях 4-5 и 8-9 мкм (облучение ионами железа) и 4-7 и 8.5-10 мкм (облучение ионами никеля) от облученной поверхности. Обнаружено перераспределение химических элементов как на поверхности, так и в объеме облученной стали, в частности, обеднение границ зерен хромом и обогащение их железом и никелем. Кроме этого, установлено радиационно-стимулированное растворение частиц второй фазы (карбидов/карбонитридов титана). При этом в объемах вокруг вакансионных пор выявлено формирование зон с повышенной концентрацией титана. Показано, что такое интенсивное растворение второй фазы в конце пробега бомбардирующих частиц отсутствует вследствие потери ими значительной доли энергии. В отличие от облучения ионами железа, при облучении ионами никеля перераспределение легирующих элементов между границами зерен и телом зерна, как и перераспределение их в локальных объемах в глубине материала, значительно менее выражены
dc.language.isoru
dc.publisherМинск : БГУ
dc.subjectЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика
dc.titleРадиационные эффекты в стали 08Х18Н10Т при облучении высокоэнергетическими ионами железа и никеля
dc.title.alternativeRadiation effects in steel 0.08C18Cr10NiTi under irradiation with high-energy iron and nickel ions / I.I. Chernov, M.S. Staltsov, B.A. Kalin, P.S. Dzhumaev, A.S. Dikov, I.A. Ivanov
dc.typeconference paper
dc.description.alternativeDevelopment of vacancy porosity, changes in the chemical and structural-phase composition of austenitic 08Cr18N10T steel were studied under irradiation by high energy Fe 10+ and Ni 11+ ions by means of transmission electron microscopy (TEM). To study the microstructure evolution over the targets depth, TEM samples were cut perpendicular to irradiated surface by the focused ion beam. A double-humped void size distribution and two swelling maxima at distances of 4-5 and 8-9 µm (irradiation by iron ions) and at distances of 4-7 and 8.5-10 µm (nickel ions) were found over the targets depth. Total swelling of irradiated samples did not exceed fractions of a percent regardless the pore nucleation depth and type of bombarding ions due to low density of voids. Redistribution of chemical elements both on the surface and in the bulk of irradiated steel was found, in particular, depletion of grain boundaries in chromium with the formation of a layer rich in chromium along the grain boundaries, and enrichment of boundaries by iron and nickel. In the deep layers of the material, the redistribution of elements is more local in nature, which may be due to the fact that the main sinks are dislocations and free surfaces of voids forming during the irradiation. It was established radiation-stimulated dissolution of second phase particles (titanium carbonitrides) in addition. In this case, the formation of zones with an increased titanium concentration was revealed in the volumes around the vacancy pores. It is shown such an intense dissolution of second phase is absent at the end of the path of bombarding particles. Redistribution of alloying elements between the grain boundaries and the grain body as well as their redistribution in local volumes in the depth of the material are much less pronounced during irradiation with nickel ions in contrast to irradiation by iron ions
Appears in Collections:2021. Взаимодействие излучений с твердым телом

Files in This Item:
File Description SizeFormat 
237-241.pdf644,11 kBAdobe PDFView/Open
Show simple item record Google Scholar



PlumX

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.