Title: Оптическое исследование модифицированных наноструктур анодно-обработанной серебряной пленки
Other Titles: Optical study modified nanostructures on the surface of anodically treated silver film / Elizaveta Konstantinova, Vasily Slezhkin, Valery Bryukhanov, Polina Medvedskaya, Ivan Lyatun
Authors: Константинова, Е. И.
Слежкин, В. А.
Брюханов, В. В.
Лятун, И. И.
Медведская, П. Н.
Keywords: ЭБ БГУ::ЕСТЕСТВЕННЫЕ И ТОЧНЫЕ НАУКИ::Физика
Issue Date: 2021
Publisher: Минск : БГУ
Citation: Взаимодействие излучений с твердым телом : материалы 14-й Междунар. конф., посвящ. 100-летию Белорус. гос. ун-та, Минск, Беларусь, 21-24 сент. 2021 г. / Белорус. гос. ун-т ; редкол.: В. В. Углов (гл. ред.) [и др.]. – Минск : БГУ, 2021. – С. 467-471.
Abstract: В работе исследовались наноструктуры анодно-обработанной серебряной пленки, модифицированные в результате адсорбции наночастицами серебра (НЧ Ag) радиусом 10 нм. Методами электронной микроскопии было установлено, что при низких концентрациях (N=0.5⸳10 13 см-2) адсорбаты НЧ распределены по поверхности относительно равномерно, при высоких (N=3.5⸳10 13 см-2) наблюдается агрегирование НЧ. В спектрах возбуждения образцов были обнаружены полосы колебаний, соответствующие как одиночным НЧ, так и агрегатам из двух и более частиц. Было установлено, что взаимодействие в агрегате имеет диполь-дипольный характер. Также при непрерывном лазерном возбуждении λ=355 нм была зарегистрирована сине-зеленая люминесценция окислов НЧ типа Ag/Ag2OxN, образованных на поверхности анодно-обработанной пленки под воздействием лазерного излучения высокой мощности
Abstract (in another language): In this work, we investigated nanostructures on the surface of an anodically treated silver film. The average size of nanostructures was 250-300 nm. Nanostructures on the surface of an anodically treated silver film were modified with silver nanoparticles (NPs) with an average radius of 10 nm by their adsorption from a hydrosol. The modified nanostructures were studied by electron and scanning probe microscopy. It was found that NPs are uniformly distributed over the surface of nanostructures, and with an increase in their concentration, NP aggregation is observed. In the excitation spectra of the samples, the vibration band Δλ = 330-350 nm, as well as vibrations at the wave-lengths of 380, 410, and 435 nm, were found. This indicates the dipole-dipole interactions between NPs and the dipole-quadrupole interaction of NPs with the nanostructure. Upon continuous laser excitation of Ag/Ag2OxN NPs by radiation with a wavelength of λ = 355 nm, blue-green luminescence with an average duration of 0.3 ms was recorded. We assume that Ag/Ag2OxN NPs were formed on the surface of the anodically treated film as a result of exposure to high-power laser radiation
Description: Секция 4. Формирование наноматериалов и наноструктур = Section 4. Formation of nanomaterials and nanostructures
URI: https://elib.bsu.by/handle/123456789/271152
ISSN: 2663-9939 (Print)
2706-9060 (Online)
Appears in Collections:2021. Взаимодействие излучений с твердым телом

Files in This Item:
File Description SizeFormat 
467-471.pdf427,03 kBAdobe PDFView/Open
Show full item record Google Scholar



PlumX

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.